TRIBOLOŠKA SVOJSTVA BORIRANIH ČELIKA
2023. urn:nbn:hr:262:255014
Krapić, Anamaria
University of Slavonski Brod

Cite this document

Krapić, A. (2023). TRIBOLOŠKA SVOJSTVA BORIRANIH ČELIKA (Master's thesis). Slavonski Brod: University of Slavonski Brod. Retrieved from https://urn.nsk.hr/urn:nbn:hr:262:255014

Krapić, Anamaria. "TRIBOLOŠKA SVOJSTVA BORIRANIH ČELIKA." Master's thesis, University of Slavonski Brod, 2023. https://urn.nsk.hr/urn:nbn:hr:262:255014

Krapić, Anamaria. "TRIBOLOŠKA SVOJSTVA BORIRANIH ČELIKA." Master's thesis, University of Slavonski Brod, 2023. https://urn.nsk.hr/urn:nbn:hr:262:255014

Krapić, A. (2023). 'TRIBOLOŠKA SVOJSTVA BORIRANIH ČELIKA', Master's thesis, University of Slavonski Brod, accessed 19 November 2024, https://urn.nsk.hr/urn:nbn:hr:262:255014

Krapić A. TRIBOLOŠKA SVOJSTVA BORIRANIH ČELIKA [Master's thesis]. Slavonski Brod: University of Slavonski Brod; 2023 [cited 2024 November 19] Available at: https://urn.nsk.hr/urn:nbn:hr:262:255014

A. Krapić, "TRIBOLOŠKA SVOJSTVA BORIRANIH ČELIKA", Master's thesis, University of Slavonski Brod, Slavonski Brod, 2023. Available at: https://urn.nsk.hr/urn:nbn:hr:262:255014

Please login to the repository to save this object to your list.
Metadata
TitleTRIBOLOŠKA SVOJSTVA BORIRANIH ČELIKA
Title (english)TRIBOLOGICAL PROPERTIES OF BORONIZED STEELS
AuthorAnamaria Krapić
MentorAndrijana Milinović (mentor)
Committee memberDaniel Novoselović (predsjednik povjerenstva)
Committee memberAndrijana Milinović (član povjerenstva)
Committee memberJosip Stojšić (član povjerenstva)
GranterUniversity of Slavonski Brod
Slavonski Brod
Defense date and country2023-09-26, Croatia
Scientific / art field,
discipline and subdiscipline		TECHNICAL SCIENCES
Mechanical Engineering
Abstract
Tema diplomskog rada je tribološka svojstva boriranih čelika. U uvodnom dijelu rada dana je osnovna podjela postupaka modificiranja površine. Opisana je tribologija i glavna područja primjene. U nastavku rada opisano je boriranje, opisane su legure koje se boriraju te su opisani postupci boriranja. U slijedećem dijelu dan je opis trošenja materijala, slučajevi trošenja te metode ispitivanja otpornosti trošenja. U eksperimentalnom dijelu rada provedeno je ispitivanje otpornosti abrazijskom trošenju boridnih slojeva. Boriranje je provedeno na čeliku C15 pri čemu je temperatura boriranja iznosila 870 °C, a trajanje 4, 6 i 8 sati. Rezultati su pokazali da su najveću otpornost imali uzorci borirani pri 870 °C.
Abstract (english)
The topic of the thesis is the tribological properties of boronized steels. In the introductory part of the paper, the basic division of surface modification procedures is given. Tribology and the main areas of application are described. In the continuation of the paper, boring is described, alloys that are boring are described and boring procedures are described. In the next part, a description of material wear, wear cases and wear resistance test methods are given. In the experimental part of the paper, testing of resistance to abrasion wear of boride layers was carried out. Boring was carried out on steel C15 where the boring temperature was 870 °C and the duration was 4, 6 and 8 hours. The results showed that the highest resistance had samples of boric at 870 °C.
Keywords
Keywords (english)
Languagecroatian
URN:NBNurn:nbn:hr:262:255014
Study programmeTitle: Graduate Study Mechanical Engineering; specializations in: Design and Product Development, Manufacturing Logistics, Materials Engineering, Engineering Technologies, Power Engineering
Course: Engineering Technologies
Study programme type: university
Study level: graduate
Academic / professional title: magistar/magistra inženjer/inženjerka strojarstva (magistar/magistra inženjer/inženjerka strojarstva)
Type of resourceText
File originBorn digital
Access conditionsAccess restricted to students and staff of home institution
Terms of useLicence In copyright icon
Created on2023-09-27 09:26:55